Code Nee. |
Chemische samenstelling % | Mechanische eigenschappen | ||||||
CU | Onzuiverheid | W | Dichtheid (g/cm3) | Hardheid HB | RES(cm) | Geleidbaarheid IACS/ % | TRS/MPa | |
CuW(50) | 50 ± 2,0 | 0,5 | Evenwicht | 11.85 | 115 | 3.2 | 54 | |
CuW(55) | 45 ± 2,0 | 0,5 | Evenwicht | 12.30 uur | 125 | 3.5 | 49 | |
CuW(60) | 40 ± 2,0 | 0,5 | Evenwicht | 12.75 uur | 140 | 3.7 | 47 | |
CuW(65) | 35 ± 2,0 | 0,5 | Evenwicht | 13.30 uur | 155 | 3.9 | 44 | |
CuW(70) | 30 ± 2,0 | 0,5 | Evenwicht | 13.80 | 175 | 4.1 | 42 | 790 |
CuW(75) | 25 ± 2,0 | 0,5 | Evenwicht | 14.50 | 195 | 4.5 | 38 | 885 |
CuW(80) | 20 ± 2,0 | 0,5 | Evenwicht | 15.15 uur | 220 | 5.0 | 34 | 980 |
CuW(85) | 15 ± 2,0 | 0,5 | Evenwicht | 15.90 | 240 | 5.7 | 30 | 1080 |
CuW(90) | 10 ± 2,0 | 0,5 | Evenwicht | 16.75 uur | 260 | 6.5 | 27 | 1160 |